Initial temperature ( M_s) of transformation decreases with the increase of cooling rate, and the final temperature ( M_f) of transformation does not change with cooling rate.

随冷却速度增大，相变开始点温度（M s）降低，相变终了点温度（M f）则不受冷却速度的影响。

This incredible rate of cooling is used to investigate the special ice crystals created during vitrification.

如此难以置信的速率用于观察研究玻璃化过程中形成的特殊冰晶体.

Calculation of Laser Amorphism Cooling Rate on Pd-Cu-Si Alloys Surface

钯-铜-硅合金表面激光非晶化冷却速率的计算

But, with increasing blowing rate from 0.8 to 1.5, the influence of the stationary vanes 'unsteady wakes on the moving blades' cooling effectiveness is reduced.

另外，吹风比从0.8增大到1.5时，静叶非定常尾迹对动叶气膜冷却效果的影响降低。

The result shows that the RE make CCT curve move towards right and hardness of steel increases at same rate of cooling.

结果表明：稀土使钢的过冷奥氏体转变曲线右移，在同样冷却速度下，加稀土钢的硬度增加。

The phase transformation and microstructure of a C-Si-Mn TRIP steel during continuous cooling after ausforming were studied by hot simulation experiment machine. The continuous cooling transformation curves were drawn using thermal dilation method, and the influence of the cooling rate on the microstructure was analyzed.

利用热/力模拟试验机研究了C-Si-Mn系TRIP钢在不同连续冷却条件下的组织变化情况，用热膨胀法绘制了动态CCT曲线，分析了冷却速度对组织的影响。

Cooling rate has much impact on the quality of freeze-dried medicine.

冻干制品对降温速率,升温速率要求很高.

The experimental results show that the critical cooling rate of pro-eutectoid ferrite is 0. 1 5 ℃/ s, and the structure of complete granular bainite can be obtained with a cooling rate from 0. 15 ℃/ s to 1 ℃/ s.

试验结果表明，本试验用钢不发生先共析铁素体析出的临界冷却速度为0.15℃／s；冷却速度在0.15～1.00℃／s范围时可得到全部粒状贝氏体组织；

The rate of change of δ 18O against temperature in the process of wet adiabatic cooling is smaller than in the process of isobaric cooling under the same humidity.

在相同的湿度条件下，湿绝热冷却过程中δ18O随温度的变化率小于等压冷却过程。

The transformed ferrite volume fraction increases and grain size decreases with the increase of cooling rate.

随着冷却速率的增加,铁素体体积分数减少,晶粒尺寸变细.

It also indicated that the liquidus temperature and the binary eutectic temperature were decreased and the ternary/ quarternary eutectic reactions and Mg_2Si phase were restrained as the cooling rate increased. The micro-hardness of the sample at the higher cooling rate was distinctly raised.

合金液相线温度和二元共晶的反应温度降低，三元或四元共晶反应被抑制，合金凝固组织中Mg2Si相的析出受到抑制，微观硬度明显提高。